S. Athithya, K. P.Mohamed Jibri, S. Harish, K. Hayakawa, Y. Kubota, H. Ikeda, Y. Hayakawa, Y. Inatomi, M. Navaneethan, J. Archana
Materials Research Express 10(5) 2023年5月1日 査読有り
Solid solution SnSe0.75S0.25 has potential to improve thermoelectric performance via ultra-low thermal conductivity as compared to the pristine SnSe which originates from phonon scattering due to disordered atoms of selenium (Se) and sulfur (S). SnSe0.75S0.25 and Cu-doped SnSe0.75S0.25 compounds were prepared via high energy ball milling and pelletized by a spark plasma sintering (SPS) process. Dislocation and point defects were successfully introduced by SnSe0.75S0.25. The existence of S in the Se site induced mass fluctuation which favors high-frequency phonon scattering. This leads to an impressively ultra-low thermal conductivity (κT) value of 0.258 W mK−1 at 753 K for SnSe0.75S0.25. Next, the Cu dopant was selected to enhance the electrical conductivity, which improved from 514.44 S m−1 (SnSe0.75S0.25) to 725.08 S m−1 for Sn0.98Cu0.02Se0.75S0.25 at 738 K. Interestingly, the Cu dopant induced nanoprecipitates of Cu2Se inside the grains, which further strengthens the phonon scattering. The Cu2Se nanoprecipitates and various defects at the grain boundaries contributed to a lower κT of 0.295 W mK−1 at 753 K for a Sn0.94Cu0.06Se0.75S0.25 sample. Moreover, the maximum figure of merit of (ZT) ∼0.19 at 738 K was attained for the Sn0.98Cu0.02Se0.75S0.25 sample.