The dye-sensitized solar cell (DSSC) has been on the market as a permanent power source for indoor IoT edge devices. In recent years, indoor illumination technology has been experiencing a drastic transition from incandescent and fluorescent lamps toward solid-state lighting devices with light-emitting diodes (LEDs). In addition to the high power efficiency, a virtue of LEDs is their prompt response, which enables precise change of the illumination level using pulse-width modulation (PWM) of the current source, and thus PWM illumination is commonly installed in society. The light intensity change from off to on states of an LED under PWM driving is literally infinity, which causes the lighting to flicker. The lighting flicker induces not only an optical illusion but also biological effects, including serious health problems, which can be mitigated by raising the modulation frequency. Because the peak intensity of a PWM illumination can be 100 times that of the average intensity, the indoor solar cell, which has a relatively high series resistance, is expected to underperform. In this paper, the characteristics of a commercial indoor DSSC under PWM illumination are studied. It is found that while PWM illumination at low frequency seriously deteriorates the performance of the DSSC, it recovers at high frequency. The latter feature is not found in indoor amorphous-Si solar cells, and the electrochemical impedance spectroscopy revealed that it stems from the electrochemical nature of some components of the series impedance in the DSSC, offering a key piece of evidence of the superiority for use in the modern indoor application of the DSSC over traditional amorphous-Si solar cells.

Abstract Electrophoretic deposition provides material-efficient film formation on large area electrodes. In this study, it has been found that there is a significant difference in the colloidal particle formation process between a thiophene-based copolymer poly(3-octylthiophene- 2,5-diyl-co-3-decyloxythiophene-2,5-diyl) (POT-co-DOT) and C₆₀ in preparation of suspension for electrophoretic deposition by reprecipitation method. This difference is attributed to the difference between low molecular weight materials with specific molecular weight and polymers with molecular weight distribution. The composition of POT-co-DOT:C₆₀ composite film by electrophoretic deposition has also been estimated.